How Neodymium magnets are made

Posted: 17th April 2018 by iulian207 in Projects








The method for manufacturing Neodymium Iron Boron magnets is as follows:

  • MELTING OF THE ALLOY UNDER VACUUM The Neodymium metal element is initially separated from refined Rare Earth oxides in an electrolytic furnace. The Neodymium, Iron and Boron and the other chemical elements are weighted  and put in a vacuum induction furnace to form an alloy. The mixture is melted due to the high frequency heating.


  • CASTING AND MILLING In simplified terms, the “Neo” alloy is like a cake mixture with each factory having its own recipe for each grade. The resultant melted alloy is then cooled to form ingots of alloy or cooled down by the so called „strip casting process“. The alloy ingots or the strip cast faces respectively are then broken down by hydrogen depreciation (HD) and then jet milled down in a nitrogen and argon atmosphere to a micron sized powder (about 3 microns or less in size). This Neodymium powder is then fed into a container, and oriented by a magnetic field in order to allow the pressing of the so called green compacts of the magnets.


  • PRESSING AND ALIGNMENT IN MAGNETIC FIELD There are three main methods of pressing the powder: isostatical pressing, axial pressing and transverse pressing. Die pressing requires tooling to make a cavity that is slightly larger than the required shape (because sintering causes shrinkage of the magnet). The Neodymium powder enters in the die cavity from the container  and is then compacted in the presence of an externally applied magnetic field. The external field is either applied parallel to the compacting force or perpendicular to the direction of compaction. Transverse pressing gives higher magnetic properties for the NdFeB sintered magnets. The other method of pressing is isostatic pressing. The NdFeB powder is put into a rubber mold and is put into a large fluid fled container which then has the pressure of the fluid increased. Again an external magnetizing feld is present but the NdFeB powder is compacted from all sides. Isostatic pressing gives the best possible magnetic performance for Neodymium Iron Boron. The methods employed vary depending on the grade of “Neo” required and are decided by the manufacturer. The external magnetizing field is created by a solenoid coil set either side of the compacting powder.

The individual powder particles of the NdFeB powder align with the magnetizing field that is applied – the more homogeneous the applied field, the more homogeneous the magnetic performance of the Neodymium magnet. As the Neodymium powder is pressed by the die, the direction of magnetization is locked in place – the Neodymium magnet has been given a preferred direction of magnetization and is called an-isotropic Rare Earth magnets exhibit uni-axial magneto-crystalline anisotropy i.e. they have a unique axis crystal structure corresponding with the easy axis of magnetization. In the case of Nd2Fe14B, the easy axis of magnetization is the c-axis of the complex tetragonal structure. In the presence of an external magnetizing field, it aligns along the c-axis, becoming capable of being fully magnetized to saturation with a very high coercivity.


  • SINTERING AND ANNEALING The  Neodymium magnet is then sintered to give it its final magnetic properties. The sintering process is carefully monitored (a strict temperature and time profle has to be applied) and occurs in an inert (oxygen free) atmosphere (e.g. argon). If oxygen is present, the resultant oxides destroy the magnetic performance of the NdFeB. The sintering process also causes shrinkage of the magnet as the powder fuses together. The shrinkage gives a magnet close to the required shape but the shrinkage is usually uneven (e.g. a ring may shrink to become an oval). At the end of the sintering process a fnal rapid quench is applied to rapidly cool the magnet. This is to minimize the unwanted production of other magnetic phases. A rapid quench maximizes the magnetic performance of NdFeB. Because the sintering process causes an uneven shrinkage, the shape of the Neodymium magnet will not be to the required dimensions.


  • MACHINING The next stage is to machine the magnets to the required tolerances. Because machining is required, the Neodymium magnets are made slightly larger when being pressed e.g. larger outer diameter, smaller inner diameter and taller for a ring magnet. Standard magnet dimensional tolerances are +/-0.1mm although +/-0.05mm is achievable at extra cost. The possibility of even tighter tolerances depends on the shape and size of the magnet and may not be achievable. For note, the Neodymium magnet is very hard. Trying to cut holes in NdFeB with a standard drill or carbide tip will blunt the drill bit. Diamond cutting tools (CNC diamond grinding wheels, diamond drills, etc.) and wire cutting machines (EDM) have to be used. The NdFeB swarf powder produced during machining needs to be cooled by liquid otherwise it may spontaneously combust. For Neodymium block magnets, there may be cost savings in using much larger magnet blocks made by isostatic pressing and cutting them into smaller Neodymium blocks of the desired size. This is done for speed and for mass production (where enough cutting and grinding machines are present) and is known as “slice and dice”. COATING Once the final dimensions for the magnet has been met by machining, the Neodymium magnet is given a protective coating. This is usually a passivization of the surface or a Ni-Cu-Ni coating. Other coatings may be possible. It is not recommended to use the magnet without any protective layer.


  1. Rohan says:

    Hey Sir.

    love your work, and would like to know if you can help me.i want to build a e-scooter what would be the best motor power and efficiency ?

    please note i would like to have more power than the avarage.
    range must be like 80 kilometers

    my regards.

  2. Drill says:

    Hey Rohan.
    You don’t need a scooter.
    One grenade would sufice.
    Best regards.